Electrical properties of La0.6Sr0.4Co0.8Fe0.2O3-δ ceramic synthesized by solid-state reaction method

Yandong Wang, Xinlong Li

Department of Materials Science and Engineering, Jilin Institute of Chemical Technology, 132022 Jilin, China


La0.6Sr0.4Co0.8Fe0.2O3-δ ceramics was prepared by means of the solid-state reaction method under the sintering condition of 1100°C for 5 h. The X-ray diffraction and Raman spectroscopy results indicated that the sample possessed a pseudo-cubic structure. The temperature-dependent electrical conductivity was measured by the dc four-electrode technique, and the calculated activation energy was 9.64 kJ/mol based on the Arrhenius relationship. The electrical conductivity relaxation data of the sample under different oxygen partial pressures (0.1-0.2 kPa) were analyzed and the surface emission coefficients at 600°C, 700°C and 800°C were obtained.

ceramics, solid-state reaction method, electrical properties, XRD, Raman, electrical conductivity relaxation.
1. S.Darvish, C.Wang, S.Jiang, Electrochim. Acta. 287, 68 (2018).
2. J.Vero, K.Bagarinao, H.Kishimoto et al., J. Electrochem.Soc., 164, F259 (2017).
3. J.Castro, N.Robles, J.A.Soltani et al., Mater. Chem.Phys.. 225, 50 (2019).
4. W.G.Wang, M.Mogensen, Solid State Ionics, 176, 457 (2005).
5. Y.D.Wang, Z.Lv, B.Wei. J. Inorg. Mater., 25, 635 (2010).
6. R.Ganeshananthan, A.V.Virkar, J. Electrochem. Soc., 152, A1620 (2005).
7. A.Aman, R.Jordan, Y.Chen et al., J. Europ. Ceram. Soc. 37, 1563 (2017).
8. V.P.Junior, P.L.Rachadel, M.N.Quadri et al. Ceram. Intern., 44, 20671 (2018).
9. G.Kostogloudis, C.Ftikos. Solid State Ionics, 126, 143 (1999).
10. L.W.Tai, M.M.Nasrallah, H.U.Anderson et al., Solid State Ionics, 76, 259 (1995).

Current number: